dc.description.abstract |
Bu çalışmada, bor parçacıkları ile takviye edilmiş tek yön cam fiber/polyester reçineli, tek yön karbon fiber/polyester reçineli, çift yön cam fiber/polyester reçineli ve çift yön karbon fiber polyester reçineli kompozit malzemelerin mekanik ve tribolojik özellikleri deneysel yöntemlerle araştırılmıştır. Bor parçacığı olarak özgül ağırlığı 1,51 g/cm3 ve molekül ağırlığı 61,83 g/mol olan borik asit parçacıkları karıştırılmış polyester reçine kullanılarak, el yatırma yöntemi ile kompozit levhalar üretilmiştir. Parçacık takviyesi olarak ağırlıkça %1, %5 ve %10 oranlarında borik asit polyester reçine karışımı elde edilmiştir. Parçacık takviyesinin mekanik özellikler üzerine etkileri araştırılmıştır. Deneysel çalışmalar sonucunda parçacık oranının artmasına bağlı olarak aşınma direncinin bazı numunelerde neutral numunelere oranla %5 ile %50 oranları arasında arttığı ve yine bazı numunelerde çekme mukavemet dayanımının %32 seviyelerine kadar iyileştiği sonuçları belirlenmiştir. Anahtar Kelimeler: Aşınma Dayanımı, Borik Asit, Çekme Testi, Hibrit Kompozit Malzemeler, Kompozit Malzemeler |
|
dc.description.abstract |
In this study, the mechanical and tribological properties of unidirectional glass fiber/polyester resin, unidirectional carbon fiber/polyester resin, bidirectional glass fiber/polyester resin and bidirectional carbon fiber/polyester resin composite materials reinforced with boron particles have been investigated by experimental methods. Composite sheets were produced by hand lay-up method using polyester resin mixed with boric acid particles (H3BO3) with a specific gravity of 1.51 g/cm3 and a molecular weight of 61.83 g/mol, which were utilized as boron particles. As particle reinforcement, 1%, 5% and 10% boric acid polyester resin mixture was obtained. The effects of particle reinforcement on mechanical and tribological properties were investigated. As a result of the experimental studies, it was determined that, due to the increase in the particle ratio, the wear resistance increased by between the ratios 5% and 50% in some samples compared to the samples not reinforced with boric acid particles and the tensile strength improved up to 32% in some samples. Keywords: Wear Resistance, Boric Acid, Tensile Test, Hybrid Composite Materials, Composite Materials |
|
dc.language.iso |
tur |
|
dc.publisher |
Kocaeli Üniversitesi, Fen Bilimleri Enstitüsü |
|
dc.rights |
openAccess |
|
dc.subject |
Aşınma dayanımı |
|
dc.subject |
Borik asit |
|
dc.subject |
Çekme testi |
|
dc.subject |
Hibrit kompozit malzemeler |
|
dc.subject |
Kompozit malzemeler. |
|
dc.subject |
Wear resistance |
|
dc.subject |
Boric acid |
|
dc.subject |
Tensile test |
|
dc.subject |
Hybrid composite materials |
|
dc.subject |
Composite materials. |
|
dc.title |
Bor parçacık katkılı kompozit malzemelerin mekanik ve tribolojik özelliklerinin araştırılması |
|
dc.title.alternative |
Investıgatıon of the mechanıcal and trıbologıcal propertıes of borıc acıd reınforced composıte materıals |
|